The corrosion behaviors of the ArF excimer laser copper alloy electrodes were studied. The morphology, composition and impurities were characterized by optical microscope, scanning electron microscopy, electron microprobe and glow discharge mass spectrometer methods. The anode produces the reef, the corrosion pits, the hole layer and the $1{-}10~\unicode[STIX]{x03BC}\text{m}$ level flake impurity. The cathode produces the particles, the sputtering pits, the element reduce layer and the $1~\unicode[STIX]{x03BC}\text{m}$ level particle impurity. Besides the Cu element, other elements in the alloy participate in the corrosion: Al element in the reef is over 1.5 times of the anode, Zn element in the particles is 1.3 times of the cathode, many trace elements congregate on the copper surface several and even hundreds of times. These elements are responsible to a great degree for the impurities and the rapid energy decline of the long-time idled laser.

The ablation of sintered silicon carbide ceramics by an ArF excimer laser was studied. Three zones are generated: the ablation zone that presented molten morphology and was composed by the Si and C phase; the condensation zone formed by vaporized SiC; and the oxidation zone that showed the characteristics of thermal oxidation. The ablation depth and oxidation range increase linearly with fluence and pulses within 0.5–4 J/cm², but the normalized ablation efficiency is constant (3.60 ± 0.60 μm·mm²/J). The theoretical photochemical ablation depth supplies 25% of the total depth at 1 J/cm² but decreases to 16% at 4 J/cm². The ablation is dominated by the photothermal effect and conforms to the thermal evaporation mechanism.